LATI Latamid 6 H2 G/30-V0AF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/30-V0AF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa

@Temperature 150 °C
 5800 psi

@Temperature 302 °F
50.0 MPa

@Temperature 120 °C
 7250 psi

@Temperature 248 °F
65.0 MPa

@Temperature 90.0 °C
 9430 psi

@Temperature 194 °F
90.0 MPa

@Temperature 60.0 °C
 13100 psi

@Temperature 140 °F
130 MPa

@Temperature 23.0 °C
 18900 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
5.0 %

@Temperature 60.0 °C
 5.0 %

@Temperature 140 °F
6.5 %

@Temperature 90.0 °C
 6.5 %

@Temperature 194 °F
7.5 %

@Temperature 120 °C
 7.5 %

@Temperature 248 °F
8.0 %

@Temperature 150 °C
 8.0 %

@Temperature 302 °F
Tensile Modulus 3.60 GPa

@Temperature 150 °C
 522 ksi

@Temperature 302 °F
4.30 GPa

@Temperature 120 °C
 624 ksi

@Temperature 248 °F
5.30 GPa

@Temperature 90.0 °C
 769 ksi

@Temperature 194 °F
7.80 GPa

@Temperature 60.0 °C
 1130 ksi

@Temperature 140 °F
11.0 GPa

@Temperature 23.0 °C
 1600 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Vicat Softening Point 210 °C

@Load 5.00 kg
 410 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 29 %
29 %
Glow Wire Test 850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWIT
850 °C

@Thickness 2.00 mm
 1560 °F

@Thickness 0.0787 in
 GWIT
930 °C

@Thickness 1.00 mm
 1710 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 525 V
525 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa