LATI Latamid 6 E02 PA 6, Impact modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 E02 PA 6, Impact modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6). Toughened. Good impact resistance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
Linear Mold Shrinkage, Flow 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Linear Mold Shrinkage, Transverse 0.0125 - 0.015 cm/cm
0.0125 - 0.015 in/in
Mechanical Properties Metric English Comments
Elongation at Break >= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
Tensile Modulus 0.150 GPa

@Temperature 150 °C
 21.8 ksi

@Temperature 302 °F
0.200 GPa

@Temperature 120 °C
 29.0 ksi

@Temperature 248 °F
0.320 GPa

@Temperature 90.0 °C
 46.4 ksi

@Temperature 194 °F
0.450 GPa

@Temperature 60.0 °C
 65.3 ksi

@Temperature 140 °F
2.00 GPa

@Temperature 23.0 °C
 290 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
Charpy Impact, Notched 10.0 J/cm²
47.6 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 55.0 °C
131 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Vicat Softening Point 175 °C

@Load 5.00 kg
 347 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 60.0 - 70.0 °C
140 - 158 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa