LATI Latamid 6 CUVHPX10 G/35 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 CUVHPX10 G/35 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. High viscosity. Toughened. Glass fibers. Heat stabilized. UV stabilized. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.0095 cm/cm
0.0070 - 0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa

@Temperature 150 °C
 7980 psi

@Temperature 302 °F
65.0 MPa

@Temperature 120 °C
 9430 psi

@Temperature 248 °F
80.0 MPa

@Temperature 90.0 °C
 11600 psi

@Temperature 194 °F
105 MPa

@Temperature 60.0 °C
 15200 psi

@Temperature 140 °F
155 MPa

@Temperature 23.0 °C
 22500 psi

@Temperature 73.4 °F
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
5.5 %

@Temperature 60.0 °C
 5.5 %

@Temperature 140 °F
6.0 %

@Temperature 90.0 °C
 6.0 %

@Temperature 194 °F
6.5 %

@Temperature 120 °C
 6.5 %

@Temperature 248 °F
7.0 %

@Temperature 150 °C
 7.0 %

@Temperature 302 °F
Elongation at Yield 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
5.0 %

@Temperature 60.0 °C
 5.0 %

@Temperature 140 °F
5.8 %

@Temperature 90.0 °C
 5.8 %

@Temperature 194 °F
6.0 %

@Temperature 120 °C
 6.0 %

@Temperature 248 °F
6.0 %

@Temperature 150 °C
 6.0 %

@Temperature 302 °F
Tensile Modulus 3.20 GPa

@Temperature 150 °C
 464 ksi

@Temperature 302 °F
3.60 GPa

@Temperature 120 °C
 522 ksi

@Temperature 248 °F
4.60 GPa

@Temperature 90.0 °C
 667 ksi

@Temperature 194 °F
6.10 GPa

@Temperature 60.0 °C
 885 ksi

@Temperature 140 °F
9.30 GPa

@Temperature 23.0 °C
 1350 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
6.30 J/cm²

@Temperature -20.0 °C
 30.0 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.650 J/cm²

@Temperature -20.0 °C
 3.09 ft-lb/in²

@Temperature -4.00 °F
0.950 J/cm²

@Temperature 23.0 °C
 4.52 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 215 °C

@Load 5.00 kg
 419 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 230 - 260 °C
446 - 500 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa