LATI Latamid 12 H2 K/30 PA 12, 30% Carbon Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 12 H2 K/30 PA 12, 30% Carbon Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 12 (PA12) based compound. Heat stabilized. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa

@Temperature 150 °C
 5080 psi

@Temperature 302 °F
50.0 MPa

@Temperature 120 °C
 7250 psi

@Temperature 248 °F
70.0 MPa

@Temperature 90.0 °C
 10200 psi

@Temperature 194 °F
95.0 MPa

@Temperature 60.0 °C
 13800 psi

@Temperature 140 °F
140 MPa

@Temperature 23.0 °C
 20300 psi

@Temperature 73.4 °F
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
4.5 %

@Temperature 60.0 °C
 4.5 %

@Temperature 140 °F
5.0 %

@Temperature 90.0 °C
 5.0 %

@Temperature 194 °F
5.5 %

@Temperature 120 °C
 5.5 %

@Temperature 248 °F
7.0 %

@Temperature 150 °C
 7.0 %

@Temperature 302 °F
Tensile Modulus 2.60 GPa

@Temperature 150 °C
 377 ksi

@Temperature 302 °F
3.90 GPa

@Temperature 120 °C
 566 ksi

@Temperature 248 °F
6.60 GPa

@Temperature 90.0 °C
 957 ksi

@Temperature 194 °F
7.20 GPa

@Temperature 60.0 °C
 1040 ksi

@Temperature 140 °F
15.8 GPa

@Temperature 23.0 °C
 2290 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -20.0 °C
 19.0 ft-lb/in²

@Temperature -4.00 °F
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
 3.81 ft-lb/in²

@Temperature -4.00 °F
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
Vicat Softening Point 170 °C

@Load 5.00 kg
 338 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 21 %
21 %
Processing Properties Metric English Comments
Melt Temperature 210 - 230 °C
410 - 446 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 70.0 - 90.0 °C

@Time 10800 sec
 158 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa