LATI Lasulf PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer LATI
Trade Name Lasulf
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lasulf PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polysulfone (PSU). Unfilled. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0095 cm/cm
0.0065 - 0.0095 in/in
Mechanical Properties Metric English Comments
Elongation at Break >= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 2.8 %

@Temperature 150 °C
 2.8 %

@Temperature 302 °F
3.5 %

@Temperature 120 °C
 3.5 %

@Temperature 248 °F
4.0 %

@Temperature 90.0 °C
 4.0 %

@Temperature 194 °F
4.5 %

@Temperature 60.0 °C
 4.5 %

@Temperature 140 °F
5.5 %

@Temperature 23.0 °C
 5.5 %

@Temperature 73.4 °F
Tensile Modulus 1.90 GPa

@Temperature 150 °C
 276 ksi

@Temperature 302 °F
2.00 GPa

@Temperature 120 °C
 290 ksi

@Temperature 248 °F
2.20 GPa

@Temperature 90.0 °C
 319 ksi

@Temperature 194 °F
2.30 GPa

@Temperature 60.0 °C
 334 ksi

@Temperature 140 °F
2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
Charpy Impact, Notched 0.150 J/cm²

@Temperature -20.0 °C
 0.714 ft-lb/in²

@Temperature -4.00 °F
0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
Vicat Softening Point 175 °C

@Load 5.00 kg
 347 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
V-1

@Thickness 3.00 mm
 V-1

@Thickness 0.118 in
Oxygen Index 30 %
30 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 150 V
150 V
A solution
Processing Properties Metric English Comments
Melt Temperature 290 - 320 °C
554 - 608 °F
Mold Temperature 110 - 130 °C
230 - 266 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa