LATI Lastilac SP G/17 ABS, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Lastilac |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Lastilac SP G/17 ABS, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Glass fibers. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0045 - 0.0065 cm/cm | 0.0045 - 0.0065 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa @Temperature 90.0 °C |
5080 psi @Temperature 194 °F |
|
| 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
||
| 75.0 MPa @Temperature 23.0 °C |
10900 psi @Temperature 73.4 °F |
||
| Elongation at Break | 2.9 % @Temperature 23.0 °C |
2.9 % @Temperature 73.4 °F |
|
| 3.3 % @Temperature 60.0 °C |
3.3 % @Temperature 140 °F |
||
| 5.5 % @Temperature 90.0 °C |
5.5 % @Temperature 194 °F |
||
| Tensile Modulus | 4.10 GPa @Temperature 90.0 °C |
595 ksi @Temperature 194 °F |
|
| 5.30 GPa @Temperature 60.0 °C |
769 ksi @Temperature 140 °F |
||
| 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
| Vicat Softening Point | 100 °C @Load 5.00 kg |
212 °F @Load 11.0 lb |
|
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 70.0 - 80.0 °C @Time 10800 sec |
158 - 176 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 313 Ground Alumina
- Solvay JAGUAR® C 17 Surfactant
- ExxonMobil Exterex™ A34 Synthetic Fluid
- CMW® 3 Copper Alloy
- Braskem TX7012 LDPE Blown Film Extrusion Polyethylene
- Bulk Molding Compounds tetra-DUR N 4303 Bulk Molding Compound
- BASF Pluracol® 4600 Graft Slabstock Foam Polyol
- ExxonMobil Escorene® HD-8661 HDPE, Rotational Molding Powder (discontinued **)
- Loctite® 7075 Acetone Base Activator
- Formosa Plastics Formolene® 1102KR Cast Film Polypropylene
Copyright © lookpolymers.com All Rights Reserved