LATI Lastilac AR-V0E ABS, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Lastilac
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lastilac AR-V0E ABS, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Very high dimensional stability. Very good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0065 cm/cm
0.0045 - 0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 8.00 MPa

@Temperature 90.0 °C
 1160 psi

@Temperature 194 °F
15.0 MPa

@Temperature 60.0 °C
 2180 psi

@Temperature 140 °F
35.0 MPa

@Temperature 23.0 °C
 5080 psi

@Temperature 73.4 °F
Elongation at Break 8.0 %

@Temperature 23.0 °C
 8.0 %

@Temperature 73.4 °F
50 %

@Temperature 60.0 °C
 50 %

@Temperature 140 °F
95 %

@Temperature 90.0 °C
 95 %

@Temperature 194 °F
Elongation at Yield 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
2.3 %

@Temperature 60.0 °C
 2.3 %

@Temperature 140 °F
2.3 %

@Temperature 90.0 °C
 2.3 %

@Temperature 194 °F
Tensile Modulus 1.50 GPa

@Temperature 90.0 °C
 218 ksi

@Temperature 194 °F
1.90 GPa

@Temperature 60.0 °C
 276 ksi

@Temperature 140 °F
2.30 GPa

@Temperature 23.0 °C
 334 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -20.0 °C
 16.7 ft-lb/in²

@Temperature -4.00 °F
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature -20.0 °C
 1.90 ft-lb/in²

@Temperature -4.00 °F
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 70.0 °C
158 °F
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Vicat Softening Point 95.0 °C

@Load 5.00 kg
 203 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 28 %
28 %
Glow Wire Test 725 °C

@Thickness 2.00 mm
 1340 °F

@Thickness 0.0787 in
 GWIT
850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 350 V
350 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 70.0 - 80.0 °C

@Time 10800 sec
 158 - 176 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa