LATI Larton G/40 PPS, 40% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer LATI
Trade Name Larton
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton G/40 PPS, 40% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0035 cm/cm
0.0020 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0065 cm/cm
0.0045 - 0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa

@Temperature 150 °C
 10900 psi

@Temperature 302 °F
100 MPa

@Temperature 120 °C
 14500 psi

@Temperature 248 °F
140 MPa

@Temperature 90.0 °C
 20300 psi

@Temperature 194 °F
170 MPa

@Temperature 60.0 °C
 24700 psi

@Temperature 140 °F
185 MPa

@Temperature 23.0 °C
 26800 psi

@Temperature 73.4 °F
Elongation at Break 1.4 %

@Temperature 23.0 °C
 1.4 %

@Temperature 73.4 °F
1.7 %

@Temperature 60.0 °C
 1.7 %

@Temperature 140 °F
2.0 %

@Temperature 90.0 °C
 2.0 %

@Temperature 194 °F
3.0 %

@Temperature 120 °C
 3.0 %

@Temperature 248 °F
3.4 %

@Temperature 150 °C
 3.4 %

@Temperature 302 °F
Tensile Modulus 6.80 GPa

@Temperature 150 °C
 986 ksi

@Temperature 302 °F
9.80 GPa

@Temperature 120 °C
 1420 ksi

@Temperature 248 °F
15.0 GPa

@Temperature 90.0 °C
 2180 ksi

@Temperature 194 °F
15.5 GPa

@Temperature 60.0 °C
 2250 ksi

@Temperature 140 °F
16.0 GPa

@Temperature 23.0 °C
 2320 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.80 J/cm²

@Temperature -20.0 °C
 13.3 ft-lb/in²

@Temperature -4.00 °F
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
0.900 J/cm²

@Temperature -20.0 °C
 4.28 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 44 %
44 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 125 V
125 V
A solution
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa