LATI Laramid G/35 PPA, 35% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Laramid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid G/35 PPA, 35% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0055 cm/cm
0.0030 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.105 cm/cm
0.0075 - 0.105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa

@Temperature 150 °C
 12300 psi

@Temperature 302 °F
130 MPa

@Temperature 120 °C
 18900 psi

@Temperature 248 °F
155 MPa

@Temperature 90.0 °C
 22500 psi

@Temperature 194 °F
180 MPa

@Temperature 60.0 °C
 26100 psi

@Temperature 140 °F
225 MPa

@Temperature 23.0 °C
 32600 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
2.8 %

@Temperature 60.0 °C
 2.8 %

@Temperature 140 °F
3.0 %

@Temperature 90.0 °C
 3.0 %

@Temperature 194 °F
4.4 %

@Temperature 120 °C
 4.4 %

@Temperature 248 °F
8.6 %

@Temperature 150 °C
 8.6 %

@Temperature 302 °F
Tensile Modulus 5.50 GPa

@Temperature 150 °C
 798 ksi

@Temperature 302 °F
8.50 GPa

@Temperature 120 °C
 1230 ksi

@Temperature 248 °F
10.0 GPa

@Temperature 90.0 °C
 1450 ksi

@Temperature 194 °F
12.0 GPa

@Temperature 60.0 °C
 1740 ksi

@Temperature 140 °F
13.5 GPa

@Temperature 23.0 °C
 1960 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 145 °C
293 °F
Deflection Temperature at 0.46 MPa (66 psi) 285 °C
545 °F
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Vicat Softening Point 270 °C

@Load 5.00 kg
 518 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa