LATI Laramid CE/60 PPA, 60% Mineral Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Mineral Filled
Manufacturer LATI
Trade Name Laramid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid CE/60 PPA, 60% Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Mineral filler. High dimensional stability. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0070 cm/cm
0.0045 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 150 °C
 6530 psi

@Temperature 302 °F
65.0 MPa

@Temperature 120 °C
 9430 psi

@Temperature 248 °F
95.0 MPa

@Temperature 90.0 °C
 13800 psi

@Temperature 194 °F
115 MPa

@Temperature 60.0 °C
 16700 psi

@Temperature 140 °F
130 MPa

@Temperature 23.0 °C
 18900 psi

@Temperature 73.4 °F
Elongation at Break 1.5 %

@Temperature 23.0 °C
 1.5 %

@Temperature 73.4 °F
1.7 %

@Temperature 60.0 °C
 1.7 %

@Temperature 140 °F
1.9 %

@Temperature 90.0 °C
 1.9 %

@Temperature 194 °F
3.5 %

@Temperature 120 °C
 3.5 %

@Temperature 248 °F
6.5 %

@Temperature 150 °C
 6.5 %

@Temperature 302 °F
Tensile Modulus 2.50 GPa

@Temperature 150 °C
 363 ksi

@Temperature 302 °F
5.30 GPa

@Temperature 120 °C
 769 ksi

@Temperature 248 °F
7.10 GPa

@Temperature 90.0 °C
 1030 ksi

@Temperature 194 °F
8.70 GPa

@Temperature 60.0 °C
 1260 ksi

@Temperature 140 °F
9.50 GPa

@Temperature 23.0 °C
 1380 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.00 J/cm²
4.76 ft-lb/in²
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 140 °C
284 °F
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 340 °C
590 - 644 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa