LATI Lapex A G/30 PES, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled
Manufacturer LATI
Trade Name Lapex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lapex A G/30 PES, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether Sulfone (PES) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0045 cm/cm
0.0030 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0075 cm/cm
0.0060 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 10.0 MPa

@Temperature 120 °C
 1450 psi

@Temperature 248 °F
90.0 MPa

@Temperature 150 °C
 13100 psi

@Temperature 302 °F
115 MPa

@Temperature 90.0 °C
 16700 psi

@Temperature 194 °F
125 MPa

@Temperature 60.0 °C
 18100 psi

@Temperature 140 °F
130 MPa

@Temperature 23.0 °C
 18900 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
2.1 %

@Temperature 60.0 °C
 2.1 %

@Temperature 140 °F
2.3 %

@Temperature 90.0 °C
 2.3 %

@Temperature 194 °F
2.4 %

@Temperature 120 °C
 2.4 %

@Temperature 248 °F
2.5 %

@Temperature 150 °C
 2.5 %

@Temperature 302 °F
Tensile Modulus 8.60 GPa

@Temperature 150 °C
 1250 ksi

@Temperature 302 °F
9.00 GPa

@Temperature 120 °C
 1310 ksi

@Temperature 248 °F
9.20 GPa

@Temperature 90.0 °C
 1330 ksi

@Temperature 194 °F
9.40 GPa

@Temperature 60.0 °C
 1360 ksi

@Temperature 140 °F
9.60 GPa

@Temperature 23.0 °C
 1390 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 185 °C
365 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
 428 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 40 %
40 %
Processing Properties Metric English Comments
Melt Temperature 350 - 370 °C
662 - 698 °F
Mold Temperature 140 - 165 °C
284 - 329 °F
Drying Temperature 150 - 180 °C

@Time 10800 sec
 302 - 356 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa