LATI LASTIROL TR G/10-V1 ES 10% Glass Fiber Polystyrene (PS) Structural Foam Resin (UL94 V-1)  (discontinued *

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Glass Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LASTIROL TR G/10-V1 ES 10% Glass Fiber Polystyrene (PS) Structural Foam Resin (UL94 V-1)  (discontinued *.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass fiber reinforced types have high rigidity and excellent dimensional stability.Specific Notes for this Material: UL94V-1 self-extinguishing, with halogens; 10% glass fiber; structural foam resin, for business machines to be painted; excellent dimensional stability, without sink marks.Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 0.10 %
0.10 %
at 23°C; ISO 62
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
LATI
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 32.0 MPa
4640 psi
ISO 527
20.0 MPa

@Temperature 60.0 °C
2900 psi

@Temperature 140 °F
ISO 527
Flexural Modulus 3.60 GPa
522 ksi
ASTM D790
3.30 GPa

@Temperature 60.0 °C
479 ksi

@Temperature 140 °F
ASTM D790
Izod Impact, Notched 0.300 J/cm

@Temperature -20.0 °C
0.562 ft-lb/in

@Temperature -4.00 °F
ASTM D256
0.300 J/cm

@Temperature -40.0 °C
0.562 ft-lb/in

@Temperature -40.0 °F
ASTM D256
0.550 J/cm

@Temperature 23.0 °C
1.03 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -40.0 °C
7.14 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
1.60 J/cm²

@Temperature -20.0 °C
7.61 ft-lb/in²

@Temperature -4.00 °F
DIN 53453
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
ASTM D648
Vicat Softening Point 90.0 °C
194 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
V-1

@Thickness 6.00 mm
V-1

@Thickness 0.236 in
Oxygen Index 24 %
24 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 695-2-1
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 180 - 200 °C
356 - 392 °F
Mold Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Drying Temperature 60.0 - 70.0 °C
140 - 158 °F
Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Heat Resistance - Ball Test (125°C) N
IEC 335
Heat Resistance - Ball Test (165°C) N
IEC 335
Injection Speed high
Needle Burner Test Y
1.47 mm
Y
3.05 mm