LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most important properties featured by the Larils which can therefore be used within a wide range of temperatures (-40°C / +110°C). The Larils feature exceptional resistance to hydrolysis and are therefore applicable also in contact with very hot water. Specific Notes for this Material: 20% glass fiber; excellent dimensional stability; good mechanical properties; low of linear thermal expansion coefficient; good thermal resistance. Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ISO 1183
Water Absorption 0.050 %
0.050 %
at 23°C; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
LATI
Mechanical Properties Metric English Comments
Hardness, Rockwell M 91
91
ASTM D785
Tensile Strength, Ultimate 98.0 MPa
14200 psi
ISO 527
44.0 MPa

@Temperature 120 °C
6380 psi

@Temperature 248 °F
ISO 527
72.0 MPa

@Temperature 90.0 °C
10400 psi

@Temperature 194 °F
ISO 527
87.0 MPa

@Temperature 60.0 °C
12600 psi

@Temperature 140 °F
ISO 527
Flexural Modulus 5.75 GPa
834 ksi
ASTM D790
4.40 GPa

@Temperature 120 °C
638 ksi

@Temperature 248 °F
ASTM D790
5.10 GPa

@Temperature 90.0 °C
740 ksi

@Temperature 194 °F
ASTM D790
5.40 GPa

@Temperature 60.0 °C
783 ksi

@Temperature 140 °F
ASTM D790
Izod Impact, Notched 0.650 J/cm

@Temperature -40.0 °C
1.22 ft-lb/in

@Temperature -40.0 °F
ASTM D256
0.750 J/cm

@Temperature -20.0 °C
1.41 ft-lb/in

@Temperature -4.00 °F
ASTM D256
0.750 J/cm

@Temperature 23.0 °C
1.41 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -20.0 °C
9.52 ft-lb/in²

@Temperature -4.00 °F
DIN 53453
2.00 J/cm²

@Temperature -40.0 °C
9.52 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 134 °C
273 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
ASTM D648
Vicat Softening Point 133 °C
271 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Oxygen Index 25 %
25 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 695-2-1
650 °C

@Thickness 1.00 mm
1200 °F

@Thickness 0.0394 in
IEC 695-2-1
Electrical Properties Metric English Comments
Dielectric Strength 23.0 kV/mm

@Thickness 2.00 mm
584 kV/in

@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index 225 V
225 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 270 - 280 °C
518 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 100 - 110 °C
212 - 230 °F
Requested for non-reinforced self-extinguishing types. Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Requested for non-reinforced self-extinguishing types. Drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Heat Resistance - Ball Test (125°C) Y
IEC 335
Heat Resistance - Ball Test (165°C) N
IEC 335
Injection Speed medium - high
Needle Burner Test N
1.47 mm
N
3.05 mm