LATI Kelon® B FR H CET/05-V2HF PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer LATI
Trade Name Kelon® B
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® B FR H CET/05-V2HF PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 23.0 °C
 10200 psi

@Temperature 73.4 °F
Elongation at Break 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 3.2 %
3.2 %
Tensile Modulus 0.400 GPa

@Temperature 150 °C
 58.0 ksi

@Temperature 302 °F
0.600 GPa

@Temperature 120 °C
 87.0 ksi

@Temperature 248 °F
1.00 GPa

@Temperature 90.0 °C
 145 ksi

@Temperature 194 °F
1.70 GPa

@Temperature 60.0 °C
 247 ksi

@Temperature 140 °F
4.00 GPa

@Temperature 23.0 °C
 580 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
Charpy Impact, Notched 0.350 J/cm²

@Temperature 23.0 °C
 1.67 ft-lb/in²

@Temperature 73.4 °F
0.350 J/cm²

@Temperature -20.0 °C
 1.67 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 65.0 °C
149 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 160 °C

@Load 5.00 kg
 320 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 26 %
26 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa