Kraiburg TPE THERMOLAST® K TC8PAN Thermoplastic Elastomer, Adhesion to PA  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kraiburg TPE THERMOLAST® K TC8PAN Thermoplastic Elastomer, Adhesion to PA  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Markets / Application Sectors:Electrical ToolsAutomotive InteriorAutomotive UndercarApplication Examples:HandlesSealsDesign and functional elementsVibration damping elementsAir inlet pipingStop buttonCable terminalsCup holderMaterial Advantages:For co moulded parts without patent infringementExcellent adhesion even with soft compoundsUL 94 HB listed compounds availableGood weather resistanceExcellent adhesion in coinjection moulding (depending on geometry and processing)Insert moulding is possibleNatural compounds easy to colourTactile surface (soft touch)Good flow characteristicsWide hardness range 25 - 80 Sh AAdhesion to PAInformation Provided by Kraiburg TPE Corp.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
DIN EN ISO 1183-1:2004
Mechanical Properties Metric English Comments
Hardness, Shore A 80
80
DIN 53505 / ISO 868
Tensile Strength at Break 5.00 MPa
725 psi
Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37
Elongation at Break 350 %
350 %
Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37
Peel Strength 23.0 kN/m
131 pli
to PA 6.6; Renault test D41 1916
24.0 kN/m
137 pli
to PA 6; Renault test D41 1916
Graves Tear Strength 23.0 kN/m
131 pli
DIN ISO 34-1 Method B (b)
Compression Set 29 %

@Temperature 23.0 °C,
Time 259000 sec
29 %

@Temperature 73.4 °F,
Time 72.0 hour
ISO 815
78 %

@Temperature 70.0 °C,
Time 79200 sec
78 %

@Temperature 158 °F,
Time 22.0 hour
ISO 815
90 %

@Temperature 100 °C,
Time 79200 sec
90 %

@Temperature 212 °F,
Time 22.0 hour
ISO 815
Thermal Properties Metric English Comments
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Processing Temperature 240 - 270 °C
464 - 518 °F
adhesion to PA 6
255 - 280 °C
491 - 536 °F
adhesion to PA 6.6 and polyamide
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 60.0 - 80.0 °C

@Time 7200 - 14400 sec
140 - 176 °F

@Time 2.00 - 4.00 hour
Pre drying
Descriptive Properties Value Comments
Color Natural