Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Kolon SPELLOY® KB133G15 PC + PBT Alloy Resin  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kolon SPELLOY® KB133G15 PC + PBT Alloy Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SPELLOY® is a new technology of thermoplastic Polymer alloys developed to provide unique combination of excellent mechanical properties.High impact resistance (at low temperature), good dimensional stability, high heat resistanceInformation provided by US distributor, API-Kolon.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
DIN 53479; ASTM D792
Water Absorption 0.11 %
0.11 %
DIN 53475; ASTM D570
Linear Mold Shrinkage 0.0070 - 0.0090 cm/cm
0.0070 - 0.0090 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
DIN 53505; ASTM D785
Tensile Strength, Ultimate 81.4 MPa
11800 psi
DIN 53455; ASTM D638
Elongation at Break 5.0 %
5.0 %
DIN 53455; ASTM D638
Flexural Yield Strength 137 MPa
19900 psi
DIN 53455; ASTM D790
Flexural Modulus 4.41 GPa
640 ksi
DIN 53452; ASTM D790
Izod Impact, Notched 1.18 J/cm
2.20 ft-lb/in
DIN 53453; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 450 µm/m-°C

@Temperature 20.0 °C
250 µin/in-°F

@Temperature 68.0 °F
DIN 53752; ASTM D696
Melting Point 220 °C
428 °F
DIN 53736; ASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
DIN 53461; ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 3.5

@Frequency 1e+6 Hz
3.5

@Frequency 1e+6 Hz
ASTM D150/DIN 53483
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149/DIN 53481
Arc Resistance 120 sec
120 sec
ASTM D495
Copyright © lookpolymers.com All Rights Reserved