- Kolon KOPA® KN333G45 G/F Reinforced Nylon 66
Kolon KOPA® KN333G45 G/F Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333G45 G/F Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
G/F 45% reinforcedApplications Internal gearsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength | 216 MPa | 31300 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 333 MPa | 48300 psi | ASTM D790 |
| Flexural Modulus | 12.062 GPa | 1749.4 ksi | ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm | 2.21 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 | 3.6 | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 943A PC
- Tokuyama Shapal™ SH-50 Sintered Aluminum Nitride
- Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- Covestro Makrolon® 3108 Polycarbonate, Extrusion Grade
- Dow Engage® 8130 Polyolefin Elastomer
- Arlon R37480X008 0.008" (0.203 mm) Uncured Silicone Rubber with Substrate: PTFE Coated Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved