Kolon KOPA® KN133G33HIBL G/F Reinforced Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN133G33HIBL G/F Reinforced Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 127 MPa | 18500 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 7.06 GPa | 1020 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm | 3.67 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 220 °C | 428 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTPE-2203G1 PVC
- PolyMirae Moplen HP562S Fiber (Spunbond) Grade Polypropylene
- Lucite International Diakon® MH254 Acrylic Bead Polymer, High Transparency
- SABIC Innovative Plastics LNP THERMOCOMP MF006A PP (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ PP 3720
- A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6
- Cytec (Conap) FR-1080 Conapoxy® Resin / Conacure® Hardener
- Colorite Polymers 8511 Clear Extrusion Vinyl Compound
- Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- 3M Scotch-Weld™ RT09 Retaining Compound Anaerobic Adhesives
Copyright © lookpolymers.com All Rights Reserved