Kolon KOCETAL® TC701 Mineral Reinforced Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Mineral Filled |
| Manufacturer | Kolon |
| Trade Name | Kocetal® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOCETAL® TC701 Mineral Reinforced Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Talc reinforced, improved dimensional stability. Applications: Products for high stiffness, dimensional precision. Information provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Melt Flow | 24 g/10 min | 24 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 81 | 81 | ASTM D785 |
| Tensile Strength | 65.0 MPa | 9430 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 331 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 25 FRG 5 TS PA66, 25% glass fibre, flame retardant
- Precision Polymer Engineering Z85L Hydrogenated NBR Compound
- Lotte Chemical Titan TITANEX® HB0972 High density polyethylene Hexene-1 resin
- LTL Color Compounds ColorFast® PC200 Polycarbonate
- Styrolution Luran® S 778 UV Colored ASA
- M Cubed Technologies HSC-702 Aluminum-toughened Reaction Bonded Silicon Carbide
- Universal Wire Works 2319 (AMS 4191) Aluminum Alloy Filler Metal
- Arlon AD300A Glass, PTFE and Micro-Dispersed Ceramic
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction
- 3M 9085UV Ultra High Temperature 100 HT Adhesive Transfer Tape
Copyright © lookpolymers.com All Rights Reserved