Kinlead LSS13 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Kinlead
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kinlead LSS13 Low Temperature Grade Heat Sealable Film (thickness: 20 µm).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LSS13 is a metalizing, low temperature grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has corona treatment with a low sealing temperature. It is widely used in food packaging for metallization with a low heat sealing temperature requirement.Information provided by Kinlead.
Physical Properties Metric English Comments
Thickness 20.0 microns
0.787 mil
± 3.0%; ASTM-252-78
Linear Mold Shrinkage 0.030 cm/cm
0.030 in/in
ASTM-D1204
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ASTM-D1204
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 185 %
185 %
ASTM-D882
Film Elongation at Break, TD 65 %
65 %
ASTM-D882
Coefficient of Friction 0.40
0.40
T/T-US; ASTM-D1894
0.40
0.40
T/O-US; ASTM-D1894
Film Tensile Strength at Break, MD 140 MPa
20300 psi
ASTM-D882
Film Tensile Strength at Break, TD 280 MPa
40600 psi
ASTM-D882
Heat Seal Strength 517.9 g/25 mm
1.142 lb/in
Kinlead
Heat Seal Strength Initiation Temperature 105 - 110 °C
221 - 230 °F
Kinlead
Optical Properties Metric English Comments
Haze 1.5 %
1.5 %
ASTM-D1003
Gloss 92 %
92 %
ASTM-D1003
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Descriptive Properties Value Comments
Wetting Tension (Dyn) 38
ASTM-D2578
Yield (m²/kg) 54.9
Kinlead