Kingfa PA6-RG30 Flame Retardant, 30% Glass Fiber Reinforced PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa PA6-RG30 Flame Retardant, 30% Glass Fiber Reinforced PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc

@Temperature 23.0 °C
 1.52 g/cc

@Temperature 73.4 °F
 ASTM D792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
 0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0090 cm/cm

@Temperature 23.0 °C
 0.0040 - 0.0090 in/in

@Temperature 73.4 °F
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 145 MPa
21000 psi
10mm/min; ASTM D638
Elongation at Break 2.1 %
2.1 %
10mm/min; ASTM D638
Flexural Strength 210 MPa
30500 psi
2mm/min; ASTM D790
Flexural Modulus 8.50 GPa
1230 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.15 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 2.15 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 220 °C

@Thickness 6.40 mm
 428 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 215 °C

@Thickness 6.40 mm
 419 °F

@Thickness 0.252 in
 ASTM D648
Flammability, UL94 V-0

@Thickness 0.900 mm
 V-0

@Thickness 0.0354 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 300 °C
<= 572 °F
Rear Barrel Temperature 220 - 240 °C
428 - 464 °F
Start Point: 235°C
Middle Barrel Temperature 240 - 260 °C
464 - 500 °F
Start Point: 255°C
Front Barrel Temperature 255 - 275 °C
491 - 527 °F
Start Point: 265°C
Melt Temperature 250 - 270 °C
482 - 518 °F
Start Point: 265°C
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Start Point: 50°C
Drying Temperature 90.0 - 110 °C

@Time 14400 - 21600 sec
 194 - 230 °F

@Time 4.00 - 6.00 hour
 Pre-dry
Descriptive Properties Value Comments
Glass Fiber Content (%) 30
Injection Speed Moderate to High