Kingfa JH960 HT10 Non-halogenated Flame Retardant PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JH960 HT10 Non-halogenated Flame Retardant PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Halogen free flame retardant, V-0/1.5mmExcellent balance propertiesHigh heat resistanceGood chemical resistanceGood hydrolysis resistanceSuit for paint and electo-platingDrop down resistanceApplications:LCD TV, monitor, PDPLaser printer, photocopierNotebook computer and chargerRechargeable cellAutomobile DVDPower tool and chargerTelecommunication equipmentInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc @Temperature 23.0 °C |
1.20 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
ASTM D955 |
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C |
21 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | 50mm/min; ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.20 mm, Temperature -10.0 °C |
5.99 ft-lb/in @Thickness 0.126 in, Temperature 14.0 °F |
ASTM D256 |
| 5.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
9.55 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | 1.6mm; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 275 °C | <= 527 °F | |
| Rear Barrel Temperature | 230 - 255 °C | 446 - 491 °F | Start Point: 235°C |
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Start Point: 245°C |
| Front Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Start Point: 255°C |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Start Point: 240°C |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C |
| Drying Temperature | 80.0 - 90.0 °C @Time 7200 - 14400 sec |
176 - 194 °F @Time 2.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | 30-80% |