- Kingfa JH-R2G10 P60 10% Glass Fiber Reinforced PC/ABS Alloy
Kingfa JH-R2G10 P60 10% Glass Fiber Reinforced PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JH-R2G10 P60 10% Glass Fiber Reinforced PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:UL HB @ 1.6-3.2mmExcellent balance propertiesHigh stiffnessGood size stabilityGood surface adhesionExcellent processing properties, large partsApplications:Injection moldingAutomobile instrument panelCD-ROM base pick-upOA device and partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc @Temperature 23.0 °C |
1.22 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Water Absorption | 0.12 % @Temperature 23.0 °C, Time 86400 sec |
0.12 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Temperature 23.0 °C |
0.0030 - 0.0050 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 82 | 82 | ASTM D785 |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | 10mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | 10mm/min; ASTM D638 |
| Flexural Strength | 119 MPa | 17300 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 4.35 GPa | 631 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.41 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Unnotched | 2.80 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
5.25 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | 1.6mm; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 285 °C | <= 545 °F | |
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C |
| Middle Barrel Temperature | 245 - 270 °C | 473 - 518 °F | Start Point: 255°C |
| Front Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Start Point: 260°C |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Start Point: 260°C |
| Mold Temperature | 80.0 - 130 °C | 176 - 266 °F | Start Point: 90°C |
| Drying Temperature | 100 - 110 °C @Time 14400 - 21600 sec |
212 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Back Pressure | 0.000 - 0.700 MPa | 0.000 - 102 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 10 | |
| Injection Speed | 60-90% |