- Kennametal Stellite Stellite® 190 PM with P/M Processing
Kennametal Stellite Stellite® 190 PM with P/M Processing
| Category | Metal , Nonferrous Metal , Cobalt Alloy , Superalloy |
| Manufacturer | Kennametal Stellite |
| Trade Name | Stellite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kennametal Stellite Stellite® 190 PM with P/M Processing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Adhesive wear test data: P/M 0.32.Applications: vane plugs, fuel metering pins, spacer bushings, ball (bearings) blanks, race (bearings) blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts.Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.50 g/cc | 0.307 lb/in³ | P/M (98%) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 596 | 596 | Converted from Rockwell C hardness. |
| 312 @Temperature 760 °C |
312 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 427 @Temperature 649 °C |
427 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 533 @Temperature 538 °C |
533 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Knoop | 720 | 720 | Converted from Rockwell C hardness. |
| 372 @Temperature 760 °C |
372 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 513 @Temperature 649 °C |
513 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 643 @Temperature 538 °C |
643 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Rockwell A | 80 | 80 | Converted from Rockwell C hardness. Beyond normal Rockwell B range, for comparison only. |
| Hardness, Rockwell B | 107 @Temperature 760 °C |
107 @Temperature 1400 °F |
|
| Hardness, Rockwell C | 58 | 58 | Hot hardness. |
| 34 @Temperature 760 °C |
34 @Temperature 1400 °F |
Hot hardness. | |
| 46 @Temperature 649 °C |
46 @Temperature 1200 °F |
Hot hardness. | |
| 54 @Temperature 538 °C |
54 @Temperature 1000 °F |
Hot hardness. | |
| Hardness, Vickers | 649 | 649 | Converted from Rockwell C hardness. |
| 326 @Temperature 760 °C |
326 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 454 @Temperature 649 °C |
454 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 575 @Temperature 538 °C |
575 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Tensile Strength, Ultimate | 621 MPa | 90100 psi | |
| 518 MPa @Temperature 538 °C |
75100 psi @Temperature 1000 °F |
||
| 518 MPa @Temperature 649 °C |
75100 psi @Temperature 1200 °F |
||
| 518 MPa @Temperature 760 °C |
75100 psi @Temperature 1400 °F |
||
| Elongation at Break | <= 1.0 % | <= 1.0 % | in 25.4 mm |
| <= 1.0 % @Temperature 538 °C |
<= 1.0 % @Temperature 1000 °F |
in 25.4 mm | |
| <= 1.0 % @Temperature 649 °C |
<= 1.0 % @Temperature 1200 °F |
in 25.4 mm | |
| <= 1.0 % @Temperature 760 °C |
<= 1.0 % @Temperature 1400 °F |
in 25.4 mm |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Boron, B | 1.0 % | 1.0 % | |
| Carbon, C | 3.1 % | 3.1 % | |
| Chromium, Cr | 26 % | 26 % | |
| Cobalt, Co | 42.9 % | 42.9 % | As remainder |
| Iron, Fe | <= 5.0 % | <= 5.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | <= 3.0 % | <= 3.0 % | |
| Other | <= 2.0 % | <= 2.0 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Tungsten, W | 14 % | 14 % |