Kennametal Stellite Deloro® N-6 PM cast
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Kennametal Stellite |
| Trade Name | Deloro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kennametal Stellite Deloro® N-6 PM cast.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data: P/M 17, cast 35. Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ | P/M (98%) |
| 8.48 g/cc | 0.306 lb/in³ | Theoretical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 345 | 345 | Converted from Rockwell C hardness. |
| 184 @Temperature 760 °C |
184 @Temperature 1400 °F |
Converted from Rockwell B hardness | |
| 291 @Temperature 649 °C |
291 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 320 @Temperature 538 °C |
320 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Knoop | 413 | 413 | Converted from Rockwell C hardness. |
| 215 @Temperature 760 °C |
215 @Temperature 1400 °F |
Converted from Rockwell B hardness | |
| 345 @Temperature 649 °C |
345 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 382 @Temperature 538 °C |
382 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Rockwell A | 69 | 69 | Converted from Rockwell C hardness. |
| 55 @Temperature 760 °C |
55 @Temperature 1400 °F |
Converted from Rockwell B hardness | |
| 66 @Temperature 649 °C |
66 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 68 @Temperature 538 °C |
68 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Rockwell B | 110 | 110 | Converted from Rockwell C hardness. Beyond normal Rockwell B range, for comparison only. |
| 90 @Temperature 760 °C |
90 @Temperature 1400 °F |
Hot hardness | |
| Hardness, Rockwell C | 38 | 38 | Hot hardness. |
| 31 @Temperature 649 °C |
31 @Temperature 1200 °F |
Hot hardness. | |
| 35 @Temperature 538 °C |
35 @Temperature 1000 °F |
Hot hardness. | |
| Hardness, Vickers | 362 | 362 | Converted from Rockwell C hardness. |
| 188 @Temperature 760 °C |
188 @Temperature 1400 °F |
Converted from Rockwell B hardness | |
| 302 @Temperature 649 °C |
302 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 334 @Temperature 538 °C |
334 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Modulus of Elasticity | 200 GPa | 29000 ksi |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Boron, B | 0.60 % | 0.60 % | |
| Carbon, C | 1.1 % | 1.1 % | |
| Chromium, Cr | 29 % | 29 % | |
| Cobalt, Co | <= 3.0 % | <= 3.0 % | |
| Iron, Fe | <= 3.0 % | <= 3.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 5.5 % | 5.5 % | |
| Nickel, Ni | 54 % | 54 % | As Remainder |
| Silicon, Si | <= 1.5 % | <= 1.5 % | |
| Tungsten, W | 2.0 % | 2.0 % |