Kennametal Stellite Deloro® 711 PM after P/M Processing

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Deloro®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Deloro® 711 PM after P/M Processing.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Deloro 711 is currently being developed. Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data P/M 6 mm^3, cast 26 mm^3. Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
theoretical
Mechanical Properties Metric English Comments
Hardness, Brinell 476
476
Converted from Rockwell C hardness.
394

@Temperature 538 °C
 394

@Temperature 1000 °F
 Converted from Rockwell C hardness
394

@Temperature 649 °C
 394

@Temperature 1200 °F
 Converted from Rockwell C hardness
Hardness, Knoop 574
574
Converted from Rockwell C hardness.
473

@Temperature 538 °C
 473

@Temperature 1000 °F
 Converted from Rockwell C hardness
473

@Temperature 649 °C
 473

@Temperature 1200 °F
 Converted from Rockwell C hardness
Hardness, Rockwell A 75
75
Converted from Rockwell C hardness.
72

@Temperature 538 °C
 72

@Temperature 1000 °F
 Converted from Rockwell C hardness
72

@Temperature 649 °C
 72

@Temperature 1200 °F
 Converted from Rockwell C hardness
Hardness, Rockwell C 50
50
Hot hardness.
43

@Temperature 538 °C
 43

@Temperature 1000 °F
 Hot hardness.
43

@Temperature 649 °C
 43

@Temperature 1200 °F
 Hot hardness.
Hardness, Vickers 510
510
Converted from Rockwell C hardness.
416

@Temperature 538 °C
 416

@Temperature 1000 °F
 Converted from Rockwell C hardness
416

@Temperature 649 °C
 416

@Temperature 1200 °F
 Converted from Rockwell C hardness
Tensile Strength, Ultimate 559 MPa
81100 psi
490 MPa

@Temperature 538 °C
 71100 psi

@Temperature 1000 °F
490 MPa

@Temperature 649 °C
 71100 psi

@Temperature 1200 °F
504 MPa

@Temperature 760 °C
 73100 psi

@Temperature 1400 °F
Elongation at Break <= 1.0 %
<= 1.0 %
in 25.4 mm
<= 1.0 %

@Temperature 538 °C
 <= 1.0 %

@Temperature 1000 °F
 in 25.4 mm
<= 1.0 %

@Temperature 649 °C
 <= 1.0 %

@Temperature 1200 °F
 in 25.4 mm
Component Elements Properties Metric English Comments
Boron, B <= 1.0 %
<= 1.0 %
Carbon, C 2.7 %
2.7 %
Chromium, Cr 27 %
27 %
Cobalt, Co 12 %
12 %
Iron, Fe 23 %
23 %
Molybdenum, Mo 7.0 %
7.0 %
Nickel, Ni 23 %
23 %
as balance
Tungsten, W 3.0 %
3.0 %