- Kennametal Stellite Deloro® 208 PM after P/M Processing
Kennametal Stellite Deloro® 208 PM after P/M Processing
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Kennametal Stellite |
| Trade Name | Deloro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kennametal Stellite Deloro® 208 PM after P/M Processing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Adhesive wear test data: cast 0.06 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.40 g/cc | 0.303 lb/in³ | P/M (98%) |
| 8.53 g/cc | 0.308 lb/in³ | Theoretical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 404 | 404 | Converted from Rockwell C hardness. |
| 254 @Temperature 760 °C |
254 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 337 @Temperature 649 °C |
337 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 373 @Temperature 538 °C |
373 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Knoop | 486 | 486 | Converted from Rockwell C hardness. |
| 299 @Temperature 760 °C |
299 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 402 @Temperature 649 °C |
402 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 448 @Temperature 538 °C |
448 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Rockwell A | 72 | 72 | Converted from Rockwell C Hardness. |
| 63 @Temperature 760 °C |
63 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 69 @Temperature 649 °C |
69 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 71 @Temperature 538 °C |
71 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Hardness, Rockwell B | 113 | 113 | Converted from Rockwell C Hardness. Beyond the normal Rockwell B range, for comparison only. |
| Hardness, Rockwell C | 44 | 44 | Hot hardness. |
| 25 @Temperature 760 °C |
25 @Temperature 1400 °F |
Hot hardness. | |
| 37 @Temperature 649 °C |
37 @Temperature 1200 °F |
Hot hardness. | |
| 41 @Temperature 538 °C |
41 @Temperature 1000 °F |
Hot hardness. | |
| Hardness, Vickers | 428 | 428 | Converted from Rockwell C hardness. |
| 261 @Temperature 760 °C |
261 @Temperature 1400 °F |
Converted from Rockwell C hardness | |
| 352 @Temperature 649 °C |
352 @Temperature 1200 °F |
Converted from Rockwell C hardness | |
| 393 @Temperature 538 °C |
393 @Temperature 1000 °F |
Converted from Rockwell C hardness | |
| Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
| 483 MPa @Temperature 760 °C |
70100 psi @Temperature 1400 °F |
||
| 552 MPa @Temperature 538 °C |
80100 psi @Temperature 1000 °F |
||
| 552 MPa @Temperature 649 °C |
80100 psi @Temperature 1200 °F |
||
| Elongation at Break | <= 1.0 % | <= 1.0 % | in 25.4 mm |
| <= 1.0 % @Temperature 538 °C |
<= 1.0 % @Temperature 1000 °F |
in 25.4 mm | |
| <= 1.0 % @Temperature 649 °C |
<= 1.0 % @Temperature 1200 °F |
in 25.4 mm | |
| 1.0 % @Temperature 760 °C |
1.0 % @Temperature 1400 °F |
in 25.4 mm |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Boron, B | <= 1.0 % | <= 1.0 % | |
| Carbon, C | 2.6 % | 2.6 % | |
| Chromium, Cr | 26 % | 26 % | |
| Cobalt, Co | 10 % | 10 % | |
| Iron, Fe | 12.5 % | 12.5 % | |
| Manganese, Mn | <= 0.75 % | <= 0.75 % | |
| Molybdenum, Mo | 10 % | 10 % | |
| Nickel, Ni | 24 % | 24 % | As Remainder |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Tungsten, W | 10 % | 10 % |