Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer Kazanorgsintez
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended to be processed into pressure pipes and connection elements for pipeline systems.Information Provided by Kazanorgsintez
Physical Properties Metric English Comments
Density 0.954 - 0.960 g/cc

@Temperature 23.0 °C
 0.0345 - 0.0347 lb/in³

@Temperature 73.4 °F
0.956 - 0.962 g/cc

@Temperature 20.0 °C
 0.0345 - 0.0348 lb/in³

@Temperature 68.0 °F
Volatiles <= 0.035 %
<= 0.035 %
Environmental Stress Crack Resistance >= 20 hour

@Temperature 80.0 °C
 >= 20 hour

@Temperature 176 °F
 with initial wall stress 2 MPa (on pipe samples d32 mm SDR 11)
>= 165 hour

@Temperature 80.0 °C
 >= 165 hour

@Temperature 176 °F
 with initial wall stress 4.6 MPa (on pipe samples d110 mm SDR 11)
>= 500 hour

@Temperature 80.0 °C
 >= 500 hour

@Temperature 176 °F
 with initial wall stress 4.6 MPa (on pipe samples d160 mm SDR 11)
Carbon Black Loading 2.0 - 2.5 %
2.0 - 2.5 %
Melt Flow 0.029 - 0.070 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 0.029 - 0.070 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ±10%
0.10 g/10 min

@Load 5.00 kg,
Temperature 190 °C
 0.10 g/10 min

@Load 11.0 lb,
Temperature 374 °F
5.0 - 7.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
 5.0 - 7.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield >= 21.0 MPa
>= 3050 psi
Elongation at Break >= 500 %
>= 500 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C

@Time >=1200 sec
 392 °F

@Time >=0.333 hour
Descriptive Properties Value Comments
Carbon Black Distribution Type I-II
Stability at Constant Internal Pressure 20°C; hr 2500
with initial wall stress 11.6 MPa