Kazanorgsintez PE2NT 11-285D High Density Polyethylene Composite

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer Kazanorgsintez
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kazanorgsintez PE2NT 11-285D High Density Polyethylene Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Production Method: Copolymerization of eythylene at low pressure pipes and connection elements for pipeline phase method. Application: Composition is intended to be processed into pressure pipes and connection elements for pipeline systems, and high-strength thick films with thickness of 20 microns and higher.Information Provided by Kazanorgsintez
Physical Properties Metric English Comments
Density 0.947 - 0.950 g/cc

@Temperature 23.0 °C
0.0342 - 0.0343 lb/in³

@Temperature 73.4 °F
0.949 - 0.952 g/cc

@Temperature 20.0 °C
0.0343 - 0.0344 lb/in³

@Temperature 68.0 °F
Volatiles <= 0.035 %
<= 0.035 %
Melt Flow 5.0 - 9.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 - 9.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
±10%
Mechanical Properties Metric English Comments
Tensile Strength, Yield >= 20.0 MPa
>= 2900 psi
Elongation at Break >= 600 %
>= 600 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C

@Time >=1200 sec
392 °F

@Time >=0.333 hour
Descriptive Properties Value Comments
Stability at Constant Internal Pressure 20°C; hr 2500
with initial wall stress 11.6 MPa
Stability at Constant Internal Pressure 80°C, initial wall stress 2.8 MPa, hr 1000
Stability at Constant Internal Pressure 80°C; initial wall stress 4.0 MPa, hr 165