Jackon JACKOCELL® S332 Expanded Polystyrene Packaging and Shape Molding

Category Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS)
Manufacturer Jackon GmbH
Trade Name JACKOCELL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Jackon JACKOCELL® S332 Expanded Polystyrene Packaging and Shape Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
100% Polystyrene.Pre-expansionThis is the low pentane version for densities above 25-30 kg/m3. A substantial reduced pentane emission has been made possible with S332 which will lead the industry into the future. The unique design of polystyrene chains gives less sensitivity to steam - hence accurate density control over the unique property of S332. The combination of good properties is clearly a result of high technology in combination with extensive product development.Shape MouldingThe unique design of polystyrene chains adds numerous advantages to Jackocell® S332 in high density shape molding. Fast molding cycles, good fusion, and easy to reach good surface. The additional broad molding window further reduces waste material and maintains a high quality to the extent that it can be recognized long term on productivity and financial earnings.
Physical Properties Metric English Comments
Density 0.0280 g/cc
0.00101 lb/in³
1.2 minute residence time pre-expander
0.0360 g/cc
0.00130 lb/in³
2 minute residence time pre-expander
0.0380 g/cc
0.00137 lb/in³
2.6 minute residence time pre-expander
0.0960 g/cc
0.00347 lb/in³
3.6 minute residence time pre-expander
Bead Size 0.600 - 1.00 mm
0.0236 - 0.0394 in
Mechanical Properties Metric English Comments
Flexural Strength 0.550 MPa
79.8 psi
30 g/l
1.05 MPa
152 psi
50 g/l
1.60 MPa
232 psi
70 g/l
2.05 MPa
297 psi
90 g/l
Compressive Strength 2.55 MPa
370 psi
30 g/l
4.69 MPa
680 psi
50 g/l
7.85 MPa
1140 psi
70 g/l
10.9 MPa
1580 psi
90 g/l
Chemical Properties Metric English Comments
Blowing Agent Content <= 4.0 %
<= 4.0 %
Pentane
Descriptive Properties Value Comments
Coefficient of Variation (%), max 15
Moulding Cycle Time (sec) 230
50 g/l, 24 hours @ 18°C
360
70 g/l, 24 hours @ 18°C
380
90 g/l, 24 hours @ 18°C
60
30 g/l, 24 hours @ 18°C