Jackon JACKOCELL® R411 Expanded Polystyrene Packaging and Shape Molding
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) |
| Manufacturer | Jackon GmbH |
| Trade Name | JACKOCELL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Jackon JACKOCELL® R411 Expanded Polystyrene Packaging and Shape Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
100% Polystyrene.Pre-expansionThe unique design of polystyrene chains and additive chemistry in the Jackocell® R411 gives pre-expanded beads of high dimensional stability. The R411 represents the smallest EPS beads in the Jackocell® EPS grade selection.Shape MouldingThe unique design of polystyrene chains in combination with small beads and narrow bead size distribution adds numerous advantages to Jackocell® R411 in shape moulding. Fast moulding cycles, good fusion and h eat resistance - and easy to reach good surface. The additional broad moulding window further reduces waste material and maintains high quality to the extent that it can be recognized long term on productivity and financial earnings.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0160 g/cc | 0.000578 lb/in³ | 2 minute residence time pre-expander |
| 0.0180 g/cc | 0.000650 lb/in³ | 2.4 minute residence time pre-expander | |
| 0.0210 g/cc | 0.000759 lb/in³ | 1 minute residence time pre-expander | |
| 0.0330 g/cc | 0.00119 lb/in³ | 0.5 minute residence time pre-expander | |
| Water Absorption | 4.0 % | 4.0 % | 13-20 hour silo ageing time; Volume% |
| Bead Size | 0.400 - 0.700 mm | 0.0157 - 0.0276 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 0.365 MPa | 52.9 psi | 16 hour silo aging time, 20 kg/m^3 |
| 0.368 MPa | 53.4 psi | 64 hours silo aging time, 20 kg/m^3 | |
| 0.369 MPa | 53.5 psi | 48 hour silo aging time, 20 kg/m^3 | |
| 0.370 MPa | 53.7 psi | 32 hour silo aging time, 20 kg/m^3 | |
| Compressive Strength | 1.37 MPa | 199 psi | 16 hour silo aging time, 20 kg/m^3 |
| 1.39 MPa | 202 psi | 32 hour silo aging time, 20 kg/m^3 | |
| 1.39 MPa | 202 psi | 48 hour silo aging time, 20 kg/m^3 | |
| 1.39 MPa | 202 psi | 64 hours silo aging time, 20 kg/m^3 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Blowing Agent Content | >= 6.0 % | >= 6.0 % | Pentane |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coefficient of Variation (%), max | 12 | |
| Moulding Cycle Time (sec) | 100 | 48 hour silo aging time, 20 kg/m^3 |
| 130 | 32 hour silo aging time, 20 kg/m^3 | |
| 175 | 6 hour silo aging time, 20 kg/m^3 | |
| 90 | 64 hours silo aging time, 20 kg/m^3 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ XN-418.G001-1000 Polypropylene Copolymer (PP Copolymer)
- Parker Chomerics Tecknit Consil®-N 891 Silver-Nickel Filled Silicone Elastomer
- Renegade Materials Corporation RM-5001 Cyanate Ester Prepreg, 6781 S2 Glass Fabric
- Sylvin Technologies 9604-90 Clear PVC for Injection Molding
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 180 lb
- Teknor Apex Monprene® MP-1862R Thermoplastic Elastomer
- UBE UBEPOL BR150B Synthetic Rubber (Compound)
- ExxonMobil Mobil Synturion 6
- Zoltek Panex 35® Type 65 Chopped Carbon Fiber for Engineering Thermoplastic Applications
- 3M 9500PC Double Coated Tapes with Adhesive 350
Copyright © lookpolymers.com All Rights Reserved