Jackon JACKOCELL® R312 Expanded Polystyrene Packaging and Shape Molding

Category Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS)
Manufacturer Jackon GmbH
Trade Name JACKOCELL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Jackon JACKOCELL® R312 Expanded Polystyrene Packaging and Shape Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
100% Polystyrene.Pre-expansionHigh density stability in pre-expansion, transportation and silo storage reduces opportunity losses through achieving typical lower average density during regular production. It is the unique design of polystyrene chains that gives the high strength advantages to Jackocell® R312 in pre-expansionShape MouldingFast molding cycles, good fusion, and easy to reach good surface. The additional broad moulding window further reduces waste material and maintains a high quality to the extent that it can be recognized long term on productivity and financial earnings.
Physical Properties Metric English Comments
Density 0.0160 g/cc
0.000578 lb/in³
1.2 minute residence time pre-expander
0.0200 g/cc
0.000723 lb/in³
1.1 minute residence time pre-expander
0.0210 g/cc
0.000759 lb/in³
2.4 minute residence time pre-expander
0.0330 g/cc
0.00119 lb/in³
0.5 minute residence time pre-expander
Bead Size 0.700 - 1.00 mm
0.0276 - 0.0394 in
Mechanical Properties Metric English Comments
Flexural Strength 0.315 MPa
45.7 psi
16 hour silo aging time, 20 kg/m^3
0.318 MPa
46.1 psi
32 hour silo aging time, 20 kg/m^3
0.322 MPa
46.7 psi
48 hour silo aging time, 20 kg/m^3
0.325 MPa
47.1 psi
64 hours silo aging time, 20 kg/m^3
Compressive Strength 1.24 MPa
180 psi
16 hour silo aging time, 20 kg/m^3
1.26 MPa
183 psi
32 hour silo aging time, 20 kg/m^3
1.27 MPa
184 psi
48 hour silo aging time, 20 kg/m^3
1.28 MPa
186 psi
64 hours silo aging time, 20 kg/m^3
Chemical Properties Metric English Comments
Blowing Agent Content >= 6.0 %
>= 6.0 %
Pentane
Descriptive Properties Value Comments
Coefficient of Variation (%), max 15
Moulding Cycle Time (sec) 120
6 hour silo aging time, 20 kg/m^3
65
64 hours silo aging time, 20 kg/m^3
75
48 hour silo aging time, 20 kg/m^3
95
32 hour silo aging time, 20 kg/m^3