Isoflon POM H Polyacetal H
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon POM H Polyacetal H.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good optical propertiesHigh UV resistanceAbsorbs little moistureInformation provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | DIN 53479 |
| Water Absorption | 0.16 % | 0.16 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 70.0 MPa | 10200 psi | DIN 53455 |
| Elongation at Break | 25 % | 25 % | DIN 53455 |
| Tensile Modulus | 3.20 GPa | 464 ksi | DIN 53457 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | DIN 52328 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 175 °C | 347 °F | DIN 53736 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous; DIN 52612 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | Continuous; DIN 52612 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1000 Hz |
3.7 @Frequency 1000 Hz |
DIN 53483 |
| Dielectric Strength | 20.0 - 65.0 kV/mm | 508 - 1650 kV/in | DIN 53481 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Nat. |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, Hardness 81A
- Hexion Bakelite™ PF 31 Phenolic Formaldehyde Resin, UL Listed (discontinued **)
- Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld
- A. Schulman ComAlloy® E-12672 Polyester Alloy
- A. Schulman POLYBLAK™ 4651SF Universal Black Color Concentrate, 50% Carbon Black in EVA
- Loctite® 7380 Monomer Base Activator
- Covestro Makrolon® 3103 Polycarbonate
- Asahi Kasei Thermylene® P-10FG-2100 10% Glass Fiber Reinforced
- Lucent Polymers PPC-0222 Polypropylene, Impact Modified
Copyright © lookpolymers.com All Rights Reserved