Isoflon PA 6 Polyamide 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon PA 6 Polyamide 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General use for mechanical partsGood heat resistanceEasy to useHigh moisture regainInformation provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | DIN 53479 |
| Water Absorption | 3.0 % | 3.0 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength | 70.0 MPa | 10200 psi | DIN 53455 |
| Elongation at Break | 50 % | 50 % | DIN 53455 |
| Tensile Modulus | 2.80 GPa | 406 ksi | DIN 53457 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | DIN 52328 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53736 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; DIN 52612 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous; DIN 52612 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1000 Hz |
3.7 @Frequency 1000 Hz |
DIN 53483 |
| Dielectric Strength | 16.0 - 25.0 kV/mm | 406 - 635 kV/in | DIN 53481 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Nat./Black |