Iran Petrochemical (PCC) I3S HC 7260(THE) High Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Iran Petrochemical Commercial Co. (PCC)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Iran Petrochemical (PCC) I3S HC 7260(THE) High Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
I3 is a high density polyethylene with 1-Butene as co monomer. It has low warpage, good flowability, high density, hardness and stiffness, good impact strength, and good stress cracking resistance.Applications: injection molding, crates, engineering parts, closures.Information provided by Iran Petrochemical Commercial Co.
Physical Properties Metric English Comments
Density 0.957 g/cc
0.0346 lb/in³
ISO 1183
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
23 g/10 min

@Load 5.00 kg,
Temperature 190 °C
23 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 64
64
ISO 868
Tensile Stress 30.0 MPa
4350 psi
at Break; ISO 527
Tensile Strength, Yield 29.0 MPa
4210 psi
ISO 527
Elongation at Break >= 1000 %
>= 1000 %
ISO 527
Elongation at Yield 10 %
10 %
ISO 527
Tensile Modulus 1.35 GPa
196 ksi
ISO 527
Charpy Impact, Notched 0.250 J/cm²
1.19 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Softening Point 72.0 °C
162 °F
ISO 306
Brittleness Temperature >= -80.0 °C
>= -112 °F
ASTM D746-72
Processing Properties Metric English Comments
Melt Temperature 200 - 280 °C
392 - 536 °F
Descriptive Properties Value Comments
Flexural Creep Modulus (MPa) 1550
4 point, 1 min; DIN 19537-2