Iran Petrochemical (PCC) BL 4M HM 8355 High Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Iran Petrochemical Commercial Co. (PCC)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Iran Petrochemical (PCC) BL 4M HM 8355 High Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BL4M is a high density polyethylene with 1-Butene as co monomer. It is high molar mass, easily processable, high stiffness and strength, good SCR, very good molding surface finish.Applications: jerry can, general purpose grade for large containers.Information provided by Iran Petrochemical Commercial Co.
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ISO 1183
Environmental Stress Crack Resistance 5.0 hour

@Pressure 3.50 MPa
5.0 hour

@Pressure 508 psi
ISO CD 16770
Melt Flow 0.35 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.35 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
9.5 g/10 min

@Load 21.6 kg,
Temperature 190 °C
9.5 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
ISO 868
Tensile Stress 34.0 MPa
4930 psi
at Break; ISO 527
Tensile Strength, Yield 26.0 MPa
3770 psi
ISO 527
Elongation at Break >= 800 %
>= 800 %
ISO 527
Elongation at Yield 10 %
10 %
ISO 527
Tensile Modulus 1.20 GPa
174 ksi
ISO 527
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Softening Point 80.0 °C
176 °F
ISO 306
Brittleness Temperature >= -80.0 °C
>= -112 °F
ASTM D746-72
Descriptive Properties Value Comments
Flexural Creep Modulus (MPa) 1100
4 point, 1 min; DIN 19537-2
Swell Ratio, % >115