Inno-Comp INNOPOL® CS 2-4120 20% Talc-Filled Polypropylene Block-Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 2-4120 20% Talc-Filled Polypropylene Block-Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 2-4120 is a 20% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form as well.INNOPOL® CS 2-4120 is developed for producing injection molded components.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 1.04 g/cc

@Temperature 23.0 °C
 0.0376 lb/in³

@Temperature 73.4 °F
 ISO 1183
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 27.0 MPa
3920 psi
50 mm/min; ISO 527-1,-2
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
7.00 J/cm²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.250 J/cm²

@Temperature -30.0 °C
 1.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 123 °C
253 °F
ISO 75-1,-2
Descriptive Properties Value Comments
Color Natural