Inno-Comp INNOPOL® CS 2-3522 TO BU 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 2-3522 TO BU 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 2-3522 TO BU is a 20% talc-filled, elastomer modified, UV-stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-3522 TO BU is developed for producing injection molded automotive components.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 1.04 g/cc

@Temperature 23.0 °C
0.0376 lb/in³

@Temperature 73.4 °F
ISO 1183
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 16.0 MPa
2320 psi
50 mm/min; ISO 527-1,-2
Tensile Modulus 1.40 GPa
203 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 1.45 GPa
210 ksi
2 mm/min; ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²

@Temperature -20.0 °C
7.61 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
ISO 75-1,-2
Vicat Softening Point 123 °C
253 °F
A; ISO 306
Descriptive Properties Value Comments
Color Black