Inno-Comp INNOPOL® CS 1-3610 UW Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-3610 UW Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-3610 UW is a white colored, flame retarded and UV-stabilized polypropylene homopolymer compound.INNOPOL® CS 1-3610 UW is recommended for producing electric articles by injection molding.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc @Temperature 23.0 °C |
0.0350 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.65 GPa | 239 ksi | 2 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² @Temperature -20.0 °C |
1.67 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1,-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |