Inno-Comp INNOPOL® CS 1-2120 AP 20% Talc Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-2120 AP 20% Talc Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL CS 1-2120 AP is a 20 % talc filled compound based on polypropylene homopolymer. This grade is available in natural and custom colored form.INNOPOL® CS 1-2120 AP is recommended especially for producing products, where high strength, low warpage, long term heat stability and excellent processability are required.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 230 °C |
18 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature 0.000 °C |
9.52 ft-lb/in² @Temperature 32.0 °F |
ISO 179/1eU |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.160 J/cm² @Temperature 0.000 °C |
0.761 ft-lb/in² @Temperature 32.0 °F |
ISO 179/1eA |
| 0.260 J/cm² @Temperature 23.0 °C |
1.24 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1,-2 |
| Vicat Softening Point | 96.0 °C | 205 °F | B120; ISO 306 |
| 153 °C | 307 °F | A120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Middle Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Front Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Melt Temperature | 210 - 250 °C | 410 - 482 °F | Injection |
| Mold Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-H TD 20 | ISO 1043 |
Users viewing this material also viewed the following:
- Dow Questra® WA551 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **)
- M. Holland Company PCAB250 Acrylonitrile Butadiene Styrene + PC
- Fine Organics FINAWAX VL Lubricant Additive
- SABIC Innovative Plastics Noryl NH3060 PPE+HIPS
- Saint-Gobain COHRlastic® 9255 High Performance Silicone Solid Rubber
- Elektro-Isola Etronax MMMF Phenolic, Cotton Fabric Reinforcement, Light Brown, Sheets
- AlphaGary Smokeguard™ LS III 1041 Low Smoke Polyvinyl Chloride
- Aaron Industries AAROPRENE® AEN 6600-3 Nylon 6/6 Engineered Resin
- Chevron Phillips Ryton® PR09 Polyphenylene Sulfide Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved