Ineos Styrenics Avantra® 585K Q402 Rubber Modified Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | Avantra® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics Avantra® 585K Q402 Rubber Modified Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Avantra® 585K Q402 is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical toughness. Although Avantra® 585K Q402 can be processed by any method applicable to polystyrene-based plastics, it is primarily used for extrusion/thermoforming. Avantra® 585K Q402 has the flow and surface gloss that make it suitable for coextrusion onto HIPS sheet used in durable goods applications like refrigerator liners and point of purchase displays. Unlike GPPS, Avantra® 585K Q402 produces a gloss cap that has excellent toughness with little sacrifice in surface appearance.Information provided by Ineos Styrenics.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 55 | 55 | ASTM D785 |
| Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Tensile Modulus | 2.07 GPa | 300 ksi | ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790-1 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256-A |
| Gardner Impact | 28.2 J | 20.8 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Solid, All Color |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 90 % | 90 % | 60°; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | ASTM D257 |
| Dielectric Constant | 2.5 @Frequency 100 - 1.00e+6 Hz |
2.5 @Frequency 100 - 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 155 kV/mm | 3940 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Extrusion |
| 180 - 280 °C | 356 - 536 °F | Molding |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® A-4160 HSL Polyphthalamide (PPA) (Unverified Data**)
- SABIC Innovative Plastics NORYL NH4030B PPE+HIPS (Asia Pacific)
- Master Bond EP21FRSPLV Flame Resistant Two Component Epoxy
- ExxonMobil Bicor™ 25MB666 OPP Film
- Diamond Polymers ASA S750
- Barlog Plastics KEBAFORM C 902 FA POM Copolymer unreinforced, reduced formaldehyde emission, UV-stabilized
- Arlon R33089X028 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Dow Corning SILASTIC® LS 5-8720 FLUOROSILICONE RUBBER
- SABIC Innovative Plastics LNP LUBRICOMP DL002 PC
- SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC
Copyright © lookpolymers.com All Rights Reserved