Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (Conditioned), Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer Ineos ABS
Trade Name Triax®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (Conditioned), Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Triax® KU2-3154 is mineral reinforced, easy-flowing, injection molding grade, and comes in pellets. It has reduced moisture absorption and very low warpage.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
DAM; ISO 1183
Filler Content 8 %
8 %
ISO 3451-1
Water Absorption 1.3 %
1.3 %
ISO 62
Water Absorption at Saturation 3.9 %
3.9 %
ISO 62
Linear Mold Shrinkage, Flow 0.0055 cm/cm
0.0055 in/in
Test Condition: 60x60x2; 260°C / MT 80°C; 500 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Test Condition: 60x60x2; 260°C / MT 80°C; 500 bar; ISO 294-4
Melt Flow 8.5 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 8.5 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 33.0 MPa
4790 psi
5 mm/min; ISO 527-1,-2
Tensile Strength, Yield 39.0 MPa
5660 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 100 %
>= 100 %
5 mm/min; ISO 527-1,-2
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.00 GPa
290 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 55.0 MPa
7980 psi
2 mm/min, @ 3.5% strain; ISO 178
62.0 MPa
8990 psi
2 mm/min; ISO 178
Flexural Modulus 1.80 GPa
261 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
>= 7.00 kJ/m²

@Temperature 23.0 °C
 >= 3.33 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
>= 100 kJ/m²

@Temperature 23.0 °C
 >= 47.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
>= 15.0 J/cm²

@Temperature 23.0 °C
 >= 71.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C
205 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-1,-2
Vicat Softening Point 95.0 °C

@Load 5.10 kg
 203 °F

@Load 11.2 lb
 50°C/hour; ISO 306
115 °C

@Load 1.02 kg
 239 °F

@Load 2.25 lb
 120°C/hour; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
 3.3

@Frequency 1.00e+6 Hz
 IEC 60250
5.0

@Frequency 100 Hz
 5.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 40.0 kV/mm

@Thickness 1.00 mm
 1020 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Dissipation Factor 0.040

@Frequency 1.00e+6 Hz
 0.040

@Frequency 1.00e+6 Hz
 IEC 60250
0.065

@Frequency 100 Hz
 0.065

@Frequency 100 Hz
 IEC 60250
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 294
Injection Velocity 40.0 mm/sec
1.57 in/sec
Injection Molding; ISO 294