Ineos ABS Triax® 3158 ABS + Polyamide Blend (DAM), PA66/ABS Pellets (filled)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer Ineos ABS
Trade Name Triax®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Triax® 3158 ABS + Polyamide Blend (DAM), PA66/ABS Pellets (filled).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Triax® 3158 is a PA+ABS-Blend and on-line paintable (195°C). It has very high heat resistance, reduced moisture, improved impact strength, and a low coefficient of linear thermal expansion. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Filler Content 9 %
9 %
Glass fiber / glass bead; ISO 3451-1
Linear Mold Shrinkage, Flow 0.011 cm/cm
0.011 in/in
Test Condition: 150x105x3; 280°C/MT 80°C; 500 bar; acc. ISO 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
Test Condition: 150x105x3; 280°C/MT 80°C; 500 bar; acc. ISO 2577
Melt Flow 10 g/10 min

@Load 10.0 kg,
Temperature 280 °C
 10 g/10 min

@Load 22.0 lb,
Temperature 536 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 10 %
>= 10 %
50 mm/min; ISO 527-1,-2
>= 10 %
>= 10 %
50 mm/min, Nominal; ISO 527-1,-2
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.90 GPa
421 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 50.0 MPa
7250 psi
2 mm/min, @ 3.5% strain; ISO 178
88.0 MPa
12800 psi
2 mm/min, @ 5% strain; ISO 178
Flexural Modulus 3.00 GPa
435 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 160 kJ/m²
76.1 ft-lb/in²
ISO 180-1U
Charpy Impact Unnotched 16.0 J/cm²
76.1 ft-lb/in²
ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 132 °C
270 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C
198 °F
ISO 75-1,-2
Vicat Softening Point 160 °C

@Load 5.10 kg
 320 °F

@Load 11.2 lb
 50°C/hour; ISO 306
245 °C

@Load 1.02 kg
 473 °F

@Load 2.25 lb
 120°C/hour; ISO 306
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
 3.3

@Frequency 1.00e+6 Hz
 IEC 60250
3.6

@Frequency 100 Hz
 3.6

@Frequency 100 Hz
 IEC 60250
Dissipation Factor 0.0077

@Frequency 100 Hz
 0.0077

@Frequency 100 Hz
 IEC 60250
0.0148

@Frequency 1.00e+6 Hz
 0.0148

@Frequency 1.00e+6 Hz
 IEC 60250
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 294
Injection Velocity 40.0 mm/sec
1.57 in/sec
Injection Molding; ISO 294