Ineos ABS TRIAX® 1408 GF ABS/Nylon Blend, Injection Grade, Dry as Molded (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS TRIAX® 1408 GF ABS/Nylon Blend, Injection Grade, Dry as Molded (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Injection molding grade, higher stiffness, good stress corrosion cracking resistance and chemical resistance (fuel, cleaning agents).Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³
Moisture Absorption at Equilibrium	1.8 %	1.8 %	Equilibrium at 50% RH
Melt Flow	3.0 g/10 min @Load 5.00 kg, Temperature 260 °C	3.0 g/10 min @Load 11.0 lb, Temperature 500 °F

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	59.0 MPa	8560 psi
Elongation at Break	3.1 %	3.1 %
Tensile Modulus	3.50 GPa	508 ksi
Charpy Impact Unnotched	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	54.0 µm/m-°C @Temperature 20.0 °C	30.0 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	127 µm/m-°C @Temperature 20.0 °C	70.6 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	121 °C	250 °F
Deflection Temperature at 1.8 MPa (264 psi)	94.0 °C	201 °F
Vicat Softening Point	107 °C	225 °F

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	3.7 @Frequency 1e+6 Hz	3.7 @Frequency 1e+6 Hz
	4.4 @Frequency 100 Hz	4.4 @Frequency 100 Hz
Dielectric Strength	31.0 kV/mm	787 kV/in
Dissipation Factor	0.028 @Frequency 1e+6 Hz	0.028 @Frequency 1e+6 Hz
	0.029 @Frequency 100 Hz	0.029 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V