Ineos ABS Lustran® Ultra 4115 ABS Pellets (a-methylstyrene-SAN / PC-modified), Very High Heat Grade

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Ineos ABS
Trade Name Lustran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® Ultra 4115 ABS Pellets (a-methylstyrene-SAN / PC-modified), Very High Heat Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® Ultra 4115 is very high heat grade with high impact resistance and is PC-modified. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Test Condition: 150x105x3; acc. ISO 2577
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Test Condition: 150x105x3; acc. ISO 2577
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 47.0 MPa
6820 psi
50 mm/min; ISO 527-1,-2
Elongation at Break 20 %
20 %
50 mm/min, Nominal; ISO 527-1,-2
35 %
35 %
50 mm/min; acc. ISO 527-1,-2
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.25 GPa
326 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 70.0 MPa
10200 psi
2 mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
40.0 kJ/m²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
4.20 J/cm²

@Temperature 23.0 °C
 20.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 114 °C
237 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
226 °F
ISO 75-1,-2
Vicat Softening Point 116 °C

@Load 5.10 kg
 241 °F

@Load 11.2 lb
 50°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Flame Spread 32 mm/min

@Thickness 2.00 mm
 1.3 in/min

@Thickness 0.0787 in
 US-FMVSS; ISO 3795
Glow Wire Test 700 °C

@Thickness 2.00 mm
 1290 °F

@Thickness 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
IEC 60093
Surface Resistance 2.00e+16 ohm
2.00e+16 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 60250
3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.0044

@Frequency 100 Hz
 0.0044

@Frequency 100 Hz
 IEC 60250
0.0084

@Frequency 1.00e+6 Hz
 0.0084

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A, Rating; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 40.0 mm/sec
1.57 in/sec
Injection Molding; ISO 294