Ineos ABS Lustran® LK197 ABS, Extrusion Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® LK197 ABS, Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® ABS LK197 resin is a high-gloss, medium-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). It provides a superior balance between rigidity and impact strength, as well as excellent melt strength for good thermoformability. It is easy to color with ABS color concentrates. Lustran® ABS LK197 resin is used for applications that require high gloss and higher rigidity, such as bathtubs, sinks, and shower surrounds for recreational vehicles, and interior liners for ice chests and picnic coolers.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ASTM-D792
Water Absorption 0.40 %

@Time 86400 sec
 0.40 %

@Time 24.0 hour
 ASTM-D570
Melt Flow 9.2 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 9.2 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM-D785
Tensile Strength, Yield 22.1 MPa

@Temperature 71.0 °C
 3210 psi

@Temperature 160 °F
 ASTM-D638
40.0 MPa

@Temperature 23.0 °C
 5800 psi

@Temperature 73.4 °F
 ASTM-D638
59.3 MPa

@Temperature -18.0 °C
 8600 psi

@Temperature -0.400 °F
 ASTM-D638
Tensile Modulus 1.50 GPa

@Temperature 71.0 °C
 218 ksi

@Temperature 160 °F
 ASTM-D638
2.30 GPa

@Temperature 23.0 °C
 334 ksi

@Temperature 73.4 °F
 ASTM-D638
2.60 GPa

@Temperature -18.0 °C
 377 ksi

@Temperature -0.400 °F
 ASTM-D638
Flexural Yield Strength 49.6 MPa

@Temperature 71.0 °C
 7190 psi

@Temperature 160 °F
 ASTM-D790
63.4 MPa

@Temperature 23.0 °C
 9200 psi

@Temperature 73.4 °F
 ASTM-D790
113.8 MPa

@Temperature -40.0 °C
 16510 psi

@Temperature -40.0 °F
 ASTM-D790
Flexural Modulus 1.90 GPa

@Temperature 71.0 °C
 276 ksi

@Temperature 160 °F
 ASTM-D790
2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
 ASTM-D790
2.80 GPa

@Temperature -40.0 °C
 406 ksi

@Temperature -40.0 °F
 ASTM-D790
Izod Impact, Notched 0.910 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
 1.70 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
 ASTM-D256
1.33 J/cm

@Thickness 3.20 mm,
Temperature -18.0 °C
 2.49 ft-lb/in

@Thickness 0.126 in,
Temperature -0.400 °F
 ASTM-D256
2.40 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.50 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM-D256
Impact Test 11.0 J

@Temperature -40.0 °C
 8.11 ft-lb

@Temperature -40.0 °F
 Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Peak Energy; ASTM-D3763
14.0 J

@Temperature -40.0 °C
 10.3 ft-lb

@Temperature -40.0 °F
 Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Total Energy; ASTM-D3763
19.0 J

@Temperature -18.0 °C
 14.0 ft-lb

@Temperature -0.400 °F
 Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Peak Energy; ASTM-D3763
22.0 J

@Temperature 23.0 °C
 16.2 ft-lb

@Temperature 73.4 °F
 Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Peak Energy; ASTM-D3763
24.0 J

@Temperature -18.0 °C
 17.7 ft-lb

@Temperature -0.400 °F
 Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Total Energy; ASTM-D3763
30.0 J

@Temperature 23.0 °C
 22.1 ft-lb

@Temperature 73.4 °F
 Instrumented Impact (0.5-in. dart, 3-in. clamp, 7.6 mph); Total Energy; ASTM-D3763
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Unannealed; ASTM-D648
101 °C
214 °F
Annealed; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Unannealed; ASTM-D648
94.0 °C
201 °F
Annealed; ASTM-D648
UL RTI, Electrical 60.0 °C

@Thickness 1.50 mm
 140 °F

@Thickness 0.0591 in
 UL746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.50 mm
 140 °F

@Thickness 0.0591 in
 UL746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.50 mm
 140 °F

@Thickness 0.0591 in
 UL746B
Flammability, UL94 HB

@Thickness 1.47 mm
 HB

@Thickness 0.0579 in
Flame Spread 35.6 mm/min

@Thickness 3.20 mm
 1.40 in/min

@Thickness 0.126 in
 ASTM-D635
Optical Properties Metric English Comments
Gloss 90 %
90 %
Angle 60°, Sheet; ASTM-D523
Processing Properties Metric English Comments
Rear Barrel Temperature 215 - 240 °C
419 - 464 °F
Extrusion
Middle Barrel Temperature 215 - 240 °C
419 - 464 °F
Extrusion
Front Barrel Temperature 215 - 240 °C
419 - 464 °F
Extrusion
Die Temperature 210 - 240 °C
410 - 464 °F
Melt Temperature 215 - 249 °C
419 - 480 °F
Extrusion
Roll Temperature 63.0 - 85.0 °C
145 - 185 °F
Down Stack, Middle
71.0 - 93.0 °C
160 - 199 °F
Up Stack, Bottom
77.0 - 99.0 °C
171 - 210 °F
Up Stack, Middle
82.0 - 105 °C
180 - 221 °F
Down Stack, Bottom
82.0 - 105 °C
180 - 221 °F
Up Stack, Top
82.0 - 105 °C
180 - 221 °F
Down Stack, Top
Drying Temperature 82.0 - 93.0 °C

@Time 10800 - 14400 sec
 180 - 199 °F

@Time 3.00 - 4.00 hour
Moisture Content <= 0.030 %
<= 0.030 %
Dew Point <= -29.0 °C
<= -20.2 °F
inlet air
Descriptive Properties Value Comments
Pump Ratio 1.5-2.0
Extrusion
Screw Compression Ratio 2.5-2.7
Extrusion