Ineos ABS Lustran® H604

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® H604.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Standard impact strength.,Property data per ISO test methods.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Estimated using room temperature density
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
Elongation at Yield 2.6 %
2.6 %
Tensile Modulus 2.40 GPa
348 ksi
Charpy Impact Unnotched 18.0 J/cm²
85.7 ft-lb/in²
11.0 J/cm²

@Temperature -30.0 °C
52.4 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
1.10 J/cm²

@Temperature -30.0 °C
5.24 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 0.800 µm/m-°C

@Temperature 20.0 °C
0.444 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
216 °F
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Vicat Softening Point 102 °C
216 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
Dielectric Strength 31.0 kV/mm
787 kV/in
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
0.0090

@Frequency 1e+6 Hz
0.0090

@Frequency 1e+6 Hz
Comparative Tracking Index 600 V
600 V