- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Ineos ABS Lustran® ABS M406
Ineos ABS Lustran® ABS M406
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS M406.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS M406 has very high impact strength and increased chemical and dynamic resistance. It is used for the production of molded plastic articles.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | Test Condition: 150x105x3; acc. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | Test Condition: 150x105x3; acc. ISO 2577 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 74.0 MPa | 10700 psi | ISO 2039-1 |
| Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 15 % | >= 15 % | 50 mm/min; acc. ISO 527-1,-2 |
| Elongation at Yield | 2.6 % | 2.6 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2; Parallel to Flow |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75-1,-2 |
| Vicat Softening Point | 92.0 °C @Load 5.10 kg |
198 °F @Load 11.2 lb |
50°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C | 1200 °F | GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm @Thickness 1.00 mm |
838 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0055 @Frequency 100 Hz |
0.0055 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 °C | 464 °F | Injection Molding; ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | Injection Molding; ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | Injection Molding; ISO 294 |