Ineos ABS Lustran® ABS E112LG Pellets

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® ABS E112LG Pellets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® ABS E112LG is extrusion grade for low gloss surfaces. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Test Condition: 60x60x2; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Test Condition: 60x60x2; ISO 294-4
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 65.0 MPa
9430 psi
ISO 2039-1
Tensile Strength, Yield 26.0 MPa
3770 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 15 %
>= 15 %
50 mm/min; acc. ISO 527-1,-2
Elongation at Yield 3.2 %
3.2 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 1.50 GPa
218 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 43.0 MPa
6240 psi
2 mm/min; ISO 178
Flexural Modulus 1.50 GPa
218 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 180-1A
8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1A
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179-1eU
12.0 J/cm²

@Temperature 23.0 °C
57.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179-1eA
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2; Parallel to Flow
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75-1,-2
Vicat Softening Point 98.0 °C

@Load 5.10 kg
208 °F

@Load 11.2 lb
50°C/hour; ISO 306
Electrical Properties Metric English Comments
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 36.0 kV/mm

@Thickness 1.00 mm
914 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 60250
0.0090

@Frequency 1.00e+6 Hz
0.0090

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
Injection Molding; ISO 294