- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade
Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | Test Condition: 60x60x2; ISO 294-4 |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 5.0 % | 5.0 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 6.20 GPa | 899 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-1,-2 |
| Vicat Softening Point | 106 °C @Load 5.10 kg |
223 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |